Lyocell fiber: Excellent performance and potential problems
With the continuous improvement of people's requirements for environmental protection, the amount of environmental protection stiffening agent is increasing year by year. Environmental protection stiffening agent is the basis for realizing clean production and environmental protection production process.It is a guarantee for the production of ecological and green functional finishing products. Formaldehyde-free rigid finishing is of great significance for protecting ecological environment.
Lyocell fibrination: Exploring the root of the problem
Lyocell fiber has a special core structure, thin skin thick core and the dividing line is not obvious. In the wet state, the fibers expand dramatically, causing the fabric to harden. Once subjected to friction, such as under the action of mechanical friction (such as rope dyeing, industrial fermentation washing, household washing, etc.), the surface layer will split several times along the axis, and eventually form nanoscale fibril, which will appear as white and pilling on the macro level.Lyocell crosslinking technology: Innovative solutionsThe interchain cross-linking technology of Lyocell fiber has excellent antigenic fibrination effect, which can improve the fibrination phenomenon in wet state and the anti-pilling performance in dry state. In the printing and dyeing process stage, the antigenic fibrination effect of ordinary Lyocell fiber can be achieved, which is close to the cross-linked Lyocell. The cost of ordinary Lyocell fiber and auxiliaries is much lower than that of crosslinked Lyocell. At the same time, it can cover a variety of printing and dyeing processing scenes, and is suitable for knitting, woven, yarn and loose fiber fabrics of various specifications; And does not affect the fabric feel, hydrophilic and other properties, does not contain formaldehyde, safety and environmental protection, high process stability, stable locking effect.
LINKCEL FF is suitable for the impregnation and locking of lyocell loose fibers, cheese yarns and fabrics of various specifications. It can be locked in the same bath with active dyeing or locked separately. The process is simple, the locking effect is excellent, it does not contain formaldehyde, and the process is safe and environmentally friendly.
LINKCEL FB is suitable for the pad dyeing, cold dyeing or pad dyeing of reactive dyes. The product is easy to use, has a good locking effect, does not contain formaldehyde, and the process is safe and environmentally friendly.
TF-6380A is suitable for the shaping and finishing process of lyocell fabrics. It can be compounded with various auxiliaries such as conventional softeners. The process is simple and the locking effect is good.
|
Product |
Linkcel FF
|
Linkcel FB
|
TF-6380A+TF-6380C |
|
|
Proposed dosage |
2-4%(o.wf) |
30-40gL |
40-80g/lL |
|
|
Applicable technology |
Machine tank dyeing |
Pad dyeing, cold pad batch dyeing |
Padding and shaping |
|
|
Suitable fabric |
Tatting |
Applicable |
Applicable |
Applicable |
|
|
Knitting
|
Applicable |
Applicable |
Applicable |
|
An announcement |
(1) It is recommended that FF be added first in the entire dyeing process, and the dyeing time should be 10-20 minutes. After adding the material, run it for about 10 minutes before adding other materials. (2) FF is mainly used for cellulose fibers. If the fabric contains chemical fibers, the dosage can be reduced as appropriate. |
1. When mixing with reactive dyes, FB and dyes must be fully dissolved before use. (2) FB is mainly used for cellulose fibers. If the fabric contains chemical fibers, the dosage can be reduced as appropriate . |
1. The fabric needs to be cleaned before finishing to ensure that the PH value of the fabric is 6-7. 2. If the cotton content is high, the setting temperature can be appropriately lowered to 150-160°C. 3. Cross- finishing will cause a certain loss of strength, please confirm through samples. |
|
|
Order Type
|
sample
|
mini order
|
normal order
|
larger order
|
|
Quantity
|
0.5-10KG
|
100KG-500KG
|
500KG-1000KG
|
over 5000KG
|
|
Lead time
|
1-2 days
|
5-10 days
|
15-25 days
|
over 30days
|
|
Shipping way
|
Express
|
Express or Air
|
By sea
|
By sea
|
Please note: Our products can be made to your special requirements!
){kind=link}